Compounds, Amorphous Solids, Solid Solutions and the Structure of Polymers
NaCl, CsCl, zinc blende and wurtzite
Each simple compound structure is a lattice plus a motif, and several are a close-packed array of anions with cations in a fraction of the voids. Rock salt (NaCl): the FCC lattice with Na⁺ at (0, 0, 0) and Cl⁻ at (½, 0, 0), that is, an FCC array of Cl⁻ with Na⁺ in all octahedral voids; CN 6 : 6, 4 formula units per cell. Examples: MgO, LiF, FeO. The ratio Na⁺/Cl⁻ ≈ 0.56 lies in the octahedral range. Caesium chloride: a simple cubic lattice with a two-ion motif, Cs⁺ at (0, 0, 0) and Cl⁻ at (½, ½, ½); CN 8 : 8, 1 formula unit per cell, and the ratio is close to 1. The ordered alloy β′-brass (CuZn) has the same structure.
ZnS has two polymorphs, both with cation and anion CN 4 : 4, both made of S²⁻ close-packed layers with Zn²⁺ in half of the tetrahedral voids (every second one, so that each Zn has four S neighbours and vice versa). Zinc blende (sphalerite) has the ABC stacking: an FCC lattice with a two-atom motif, 4 formula units per cubic cell, exactly the diamond structure with two kinds of atom (GaAs, CdTe, InP). Wurtzite has the AB stacking: a hexagonal lattice, 2 formula units per cell (ZnO, GaN, CdS, AlN). Their local environments are the same, and they differ only in the stacking of the layers, just as FCC differs from HCP.
| Structure | Lattice | CN (cation : anion) | Formula units per cell |
|---|---|---|---|
| NaCl | FCC | 6 : 6 | 4 |
| CsCl | Simple cubic | 8 : 8 | 1 |
| Zinc blende | FCC | 4 : 4 | 4 |
| Wurtzite | Hexagonal | 4 : 4 | 2 |
Density. ρ = (formula units per cell × M)/(V_c N_A), where M is the formula mass. NaCl, with a = 0.5640 nm, M = 22.99 + 35.45 = 58.44 g/mol: ρ = 4 × 58.44/[6.022 × 10²³ × (0.5640 × 10⁻⁷ cm)³] = 233.76/108.04 = 2.16 g/cm³. Counting 8 ions instead of 4 formula units is the usual factor-of-two slip.
Perovskite and spinel
Perovskite, ABO₃ (CaTiO₃, BaTiO₃, SrTiO₃): the large A cation (CN 12) sits at the cube corners, the small B cation (CN 6) at the body centre and O²⁻ at the three face-centre positions, so there is 1 formula unit per cell and the charges satisfy z_A + z_B = 6. Equivalently, A and O together form an FCC-like array (AO₃ layers) with B in one quarter of the octahedral voids, those surrounded only by oxygen. The ideal cubic cell has A–O distance a/√2 and B–O distance a/2, so touching ions would need (r_A + r_O) = √2 (r_B + r_O). The Goldschmidt tolerance factor t = (r_A + r_O)/[√2 (r_B + r_O)] measures the misfit; t near 1 favours the cubic structure and departures distort it. BaTiO₃ is cubic above about 120 °C and tetragonal and ferroelectric below it, since the small Ti⁴⁺ shifts off centre.
Spinel, AB₂O₄ (MgAl₂O₄, Fe₃O₄): an FCC array of O²⁻ with a cubic cell of 8 formula units, 32 O²⁻, 64 tetrahedral and 32 octahedral voids. In a normal spinel the 8 A²⁺ ions occupy 8 of the 64 tetrahedral voids (one eighth) and the 16 B³⁺ ions occupy 16 of the 32 octahedral voids (one half). In an inverse spinel the A²⁺ ions and half of the B³⁺ ions share the octahedral sites and the other half of the B³⁺ ions occupy tetrahedral sites, written B[AB]O₄. Magnetite is inverse, Fe³⁺[Fe²⁺Fe³⁺]O₄; ZnFe₂O₄ is normal.
Amorphous solids: crystalline and glassy silica, fused silica, soda-lime glass
The unit of every silica structure is the SiO₄ tetrahedron, with Si–O about 0.16 nm. Tetrahedra join only at corners, each oxygen bridging two silicon atoms, which gives the formula SiO₂. In crystalline silica (quartz, cristobalite, tridymite) the Si–O–Si angles and the way tetrahedra rotate about each other repeat, so there is long-range order and a sharp melting point. In glassy silica the tetrahedra are the same and the local order is preserved, but the bridging angles and rotations vary randomly, so there is short-range order (neighbours, bond lengths) and no long-range order. Diffraction shows sharp peaks for the crystal and broad halos for the glass.
Fused silica is pure SiO₂ glass made by melting quartz: a fully connected network with very high softening temperature (above 1500 °C) and very low thermal expansion, hence thermal-shock resistance. Soda-lime glass (windows, bottles) is roughly 70 to 75 mass % SiO₂ with Na₂O and CaO making up most of the rest. SiO₂ is the network former. Na₂O is a modifier: each Na₂O breaks a Si–O–Si bridge and creates two non-bridging oxygens that carry the Na⁺, which loosens the network, lowers the softening temperature to roughly 700 °C and makes the glass easy to form. CaO makes the glass more durable against water, since the Na⁺ alone would let it dissolve. The price is a higher thermal expansion and poorer thermal-shock resistance than fused silica.
Solid solutions and the Hume-Rothery rules
A solid solution is a single crystalline phase in which solute atoms are dissolved in the lattice of the solvent, so the structure of the solvent is kept. In a substitutional solution the solute atoms replace solvent atoms on lattice sites (Cu in Ni). In an interstitial solution the small solute atoms sit in the voids of the solvent lattice (C, N, H, O, B in iron); the void sizes of the previous chapter limit how much can dissolve, which is why carbon dissolves far more in FCC than in BCC iron. Substitutional solutions may be random or ordered.
- Size factor: the atomic radii of solute and solvent differ by less than about 15 %, where the difference is (r_solute − r_solvent)/r_solvent.
- Crystal structure: solute and solvent have the same crystal structure; this is required for complete solubility.
- Electronegativity: the two are similar; a large difference favours compound formation instead of a solution.
- Valence: other things equal, a metal dissolves more readily a metal of higher valence than one of lower valence.
Copper and nickel meet all four (radii 0.128 and 0.125 nm, a 2.3 % difference; both FCC; similar electronegativity) and are completely soluble in each other. Failing any rule limits solubility but does not forbid it: the rules are guides for substitutional systems, and an interstitial solute needs a small enough atom, not Hume-Rothery matching. A solid solution is not a mixture: the solute is dissolved at atomic scale in a single phase, and the lattice parameter changes smoothly with composition.
Polymer chains: monomers, bonding, degree of polymerisation and tacticity
A polymer is a molecule of many repeat units (mers) joined by covalent bonds; a monomer is the small molecule from which they come. In addition (chain-growth) polymerisation monomers with a C=C double bond add one after another by initiation, propagation and termination, and nothing is lost, so the repeat unit has the composition of the monomer: PE, PP, PVC, PS and PTFE. In condensation (step-growth) polymerisation bifunctional monomers react and release a small molecule, usually water or HCl, so the repeat unit has less mass than the monomers combined: nylon 6,6 from hexamethylenediamine and adipic acid (releasing water), and PET from ethylene glycol and terephthalic acid.
Bonding. Along the chain the atoms are joined by strong covalent bonds (C–C about 0.154 nm, about 350 kJ/mol, with a tetrahedral bond angle of 109.5° that makes the carbon backbone zigzag). Between chains only secondary bonds act, van der Waals forces and, where groups allow, dipole or hydrogen bonds, which are weaker by one to two orders of magnitude. This duality explains why polymers soften or melt long before any covalent bond breaks.
Degree of polymerisation. With the convention used here, DP = M̄_n/m, where M̄_n is the number-average molar mass of the polymer and m the molar mass of one repeat unit. For PVC, repeat unit –CH₂–CHCl–, m = 62.5 g/mol, so M̄_n = 50 000 g/mol gives DP = 800. Each repeat unit of a vinyl polymer adds two backbone carbons, so a chain of DP n has 2n C–C bonds; fully extended in the zigzag, each bond advances 0.154 × sin(109.5°/2) = 0.126 nm along the chain. For DP = 10 000 the extended length is 2 × 10 000 × 0.126 nm = 2.5 μm, although the real coil is far shorter.
Configuration vs conformation. Configuration is the arrangement fixed by the covalent bonds, such as the side-group placement, cis or trans geometry about a double bond; changing it requires breaking bonds. Conformation is the shape of the chain produced by rotation about single bonds, which changes freely with temperature or stress without breaking anything. For a vinyl chain –CH₂–CHR– the side groups R give three tacticities: isotactic (all R on the same side of the backbone), syndiotactic (R alternating from side to side) and atactic (R randomly placed). Regular chains (isotactic, syndiotactic) can pack in crystals; atactic chains cannot.
Crystallinity, copolymers, common polymers, crosslinking and rubber
Long chains can crystallise only by folding into thin lamellae, and a large fraction of chains remains disordered, so most crystallisable polymers are semi-crystalline (crystalline lamellae in an amorphous matrix, grouped in spherulites); a polymer whose chains are irregular is wholly amorphous. Crystallinity raises density, stiffness, melting point and opacity. It needs linear, regular chains with small side groups, and it is helped by slow cooling. Mass-fraction crystallinity from density: X_c = ρ_c(ρ_s − ρ_a)/[ρ_s(ρ_c − ρ_a)]. For polyethylene with ρ_c = 1.000 and ρ_a = 0.870 g/cm³ and a sample of ρ_s = 0.960 g/cm³: X_c = 1.000 × 0.090/(0.960 × 0.130) = 0.721, or 72.1 %.
| Polymer | Repeat unit | m (g/mol) | Structural point |
|---|---|---|---|
| PE | –CH₂–CH₂– | 28.05 | No side group; linear HDPE packs well, branched LDPE less |
| PP | –CH₂–CH(CH₃)– | 42.08 | Isotactic crystallises; atactic is soft and amorphous |
| PVC | –CH₂–CHCl– | 62.50 | Polar Cl; mostly atactic, largely amorphous |
| PTFE | –CF₂–CF₂– | 100.02 | Fluorine sheath; highly crystalline, inert, low friction |
| PS | –CH₂–CH(C₆H₅)– | 104.15 | Bulky phenyl; commercial atactic PS is amorphous and glassy |
Copolymers contain two or more kinds of mer: random (A and B in no order), alternating (ABAB…) and block (long runs of A joined to long runs of B). Random copolymerisation disturbs the regularity and usually lowers crystallinity. Crosslinking joins chains by covalent bridges into a network that can swell but cannot dissolve or flow. Natural rubber is cis-1,4-polyisoprene (repeat unit C₅H₈, 68.12 g/mol), a soft, weak material of low T_g with coiled chains; its trans isomer is the hard, crystalline gutta-percha. Vulcanisation heats rubber with sulfur, which forms bridges of one or more S atoms between chains near the C=C double bonds. A few mass percent of sulfur gives an elastic rubber that snaps back, because crosslinks stop chains from flowing past each other; much more sulfur gives the rigid ebonite.
Worked example (crosslinking). 100 g of natural rubber is vulcanised with 3.0 g S, each crosslink bridge being two S atoms joining two repeat units. Repeat units: 100/68.12 = 1.468 mol. S: 3.0/32.06 = 0.0936 mol, giving 0.0468 mol of bridges and 2 × 0.0468 = 0.0936 mol of crosslinked units. Fraction crosslinked = 0.0936/1.468 = 0.064, or 6.4 % of the repeat units.
Key takeaways
- Radius ratio r/R sets CN: 0.155–0.225 gives 3, 0.225–0.414 gives 4, 0.414–0.732 gives 6, 0.732–1 gives 8. Pauling’s second rule makes the bond strengths z/CN reaching an anion sum to its charge.
- NaCl is FCC with 4 formula units and CN 6 : 6; CsCl is simple cubic with 1 unit and CN 8 : 8; zinc blende (FCC, 4 units) and wurtzite (hexagonal, 2 units) have CN 4 : 4 and differ only in stacking.
- Perovskite ABO₃ has A at corners, B at the body centre, O at face centres, tolerance factor t = (r_A + r_O)/[√2 (r_B + r_O)]. Spinel AB₂O₄ fills 1/8 of tetrahedral and 1/2 of octahedral voids of an FCC oxygen array; inverse spinel puts half the B ions in tetrahedral sites.
- Silica is corner-sharing SiO₄ tetrahedra, ordered over long range in the crystal and only over short range in the glass. Na₂O modifies the network and lowers the softening temperature; CaO restores durability.
- Hume-Rothery: size within about 15 %, same crystal structure, similar electronegativity, favourable valence. Small atoms (C, N, H) dissolve interstitially in voids; larger ones substitute.
- Polymers: strong covalent bonds along the chain, weak secondary bonds between chains; DP = M̄_n/m; tacticity is configuration, bond rotation changes only conformation; crosslinks turn chains into a network, as sulfur does in vulcanised rubber.
Practice questions (18)
Attempt each one before opening the answer. Every explanation names the tempting wrong option as well as the right one, because that is where marks are lost.
In a strongly ionic compound the cation-to-anion radius ratio is r/R = 0.30. Pauling’s first rule (radius-ratio rule) predicts the cation to be surrounded by
Show answer
Answer: B — four anions at the corners of a tetrahedron, since the ratio lies between 0.225 and 0.414
The coordination windows are 0.155–0.225 (CN 3), 0.225–0.414 (CN 4), 0.414–0.732 (CN 6) and 0.732–1 (CN 8). A ratio of 0.30 lies in the tetrahedral window. CN 6 would need r/R of at least 0.414, so that reading, the tempting one, is wrong; CN 8 needs at least 0.732 and CN 3 applies only below 0.225.In silica each Si⁴⁺ has coordination number 4 towards O²⁻. Pauling’s electrostatic valence rule then requires every O²⁻ to be bonded to how many Si⁴⁺ ions?
Show answer
Answer: D — Two, so that each oxygen bridges two tetrahedra and receives 2 × 1 = 2
The bond strength of Si⁴⁺ is z/CN = 4/4 = 1. The bonds arriving at O²⁻ must sum to 2, so two Si⁴⁺ neighbours are needed: every oxygen is a corner shared by two SiO₄ tetrahedra, which gives SiO₂. One neighbour would give 1 and leave the oxygen under-bonded; three or four would over-bond it.Zinc blende and wurtzite are two forms of ZnS. Which statement about them is correct?
Show answer
Answer: A — Both have CN 4 : 4 with Zn²⁺ in half of the tetrahedral voids of close-packed S²⁻ layers; they differ in the layer stacking, ABC… in blende and AB… in wurtzite
Blende is the ABC (FCC) form, 4 formula units per cubic cell; wurtzite is the AB (HCP) form, 2 per hexagonal cell. In both, Zn²⁺ fills every second tetrahedral void, so the coordination is 4 : 4. The cubic/hexagonal labels are interchanged in one distractor, and the BCC claim is false because neither is a body-centred array.Which description of the rock-salt (NaCl) structure is correct?
Show answer
Answer: C — An FCC lattice with Na⁺ at (0, 0, 0) and Cl⁻ at (½, 0, 0): Na⁺ fills all octahedral voids, CN 6 : 6, four formula units per cell
NaCl is an FCC lattice with a two-ion motif. Equivalently the Cl⁻ ions form an FCC array and Na⁺ occupies all four octahedral voids per cell, giving CN 6 : 6. The simple cubic description is CsCl, filling all the tetrahedral voids would give an anti-fluorite-type arrangement, and the half-filled tetrahedral description is zinc blende.In a normal spinel AB₂O₄ the O²⁻ ions form an FCC array. Which fraction of the voids is occupied by cations?
Show answer
Answer: D — One eighth of the tetrahedral voids (A ions) and one half of the octahedral voids (B ions)
Per cell there are 32 O²⁻, 64 tetrahedral and 32 octahedral voids, with 8 A and 16 B ions. The 8 A²⁺ ions fill 8/64 = 1/8 of the tetrahedral voids, and the 16 B³⁺ ions fill 16/32 = 1/2 of the octahedral voids. The reversed fractions in the distractor swap the roles of the sites, and rock-salt filling applies to NaCl, not spinel.Adding Na₂O to silica glass lowers its softening temperature mainly because the Na₂O
Show answer
Answer: C — breaks Si–O–Si bridges into non-bridging oxygens, which loosens the network connectivity
Each Na₂O supplies an oxygen that terminates a Si–O–Si bridge, forming two non-bridging oxygens balanced by Na⁺. A less connected network softens at a lower temperature. Na⁺ does not substitute for Si⁴⁺ (the charges and sizes are wrong) and adding Na₂O reduces, not increases, the connectivity, which is what the crosslink distractor reverses.A pair of metals is expected to show complete solid solubility in each other under the Hume-Rothery rules. Which pair?
Show answer
Answer: D — Both FCC, radii 0.128 and 0.125 nm, similar electronegativity and valence
Only the pair with the close FCC radii 0.128 and 0.125 nm satisfies every rule: the same crystal structure, a size difference of 2.3 % (below 15 %), similar electronegativity and valence. The 0.128 and 0.180 nm pair differs in size by 41 %, the FCC and BCC pair in crystal structure, and the last in electronegativity, which would favour a compound rather than a solution.Which statement correctly contrasts addition and condensation polymerisation?
Show answer
Answer: D — Addition polymerisation loses no atoms, so the repeat unit has the monomer’s composition, whereas condensation polymerisation releases a small molecule such as H₂O
In addition polymerisation (PE, PVC, PS) monomers with C=C add without loss. In condensation polymerisation (nylon 6,6, PET) bifunctional monomers react and release water or HCl, so the repeat unit is lighter than the monomers combined. The other statements swap these features or invent a release step in addition polymerisation.A sample of isotactic polypropylene is heated, stretched, bent and allowed to relax, with no bond ever broken. It can then end up as which of the following?
Show answer
Answer: C — A chain of a different conformation but of the same configuration, still isotactic
Tacticity is a configuration, defined by which side of the backbone each CH₃ group is attached to, and it can change only if bonds are broken and remade. Heating, stretching and bending change only conformation through rotation about C–C bonds, so the chain stays isotactic. The atactic and syndiotactic options wrongly treat tacticity as a conformation, and removing CH₃ groups needs chemical reaction.Which polymer is most likely to be semi-crystalline under normal processing?
Show answer
Answer: B — Linear polyethylene, because it has no side groups and its chains fold regularly
Linear polyethylene has the simplest, most regular chain, so it crystallises to a high degree. Atactic polystyrene and atactic polypropylene have irregular side-group placement and stay amorphous (and the methyl groups of atactic PP are not all on one side, that is isotactic). A random copolymer with a 1 : 1 mix has little regularity.Which of the following statements about Pauling’s rules and the radius-ratio rule are correct?
Show answer
Answer: A — The sum of the electrostatic bond strengths z/CN reaching an anion equals the magnitude of the anion’s charge; B — For a strongly ionic compound with r/R = 0.50 the radius-ratio rule predicts octahedral coordination of the cation
The valence rule and the 0.414 to 0.732 window for CN 6 are both correct. The third rule says corner sharing is preferred, then edges, then faces, because shared faces bring cations too close and raise repulsion. ZnS has substantial covalent character, so the radius-ratio rule is not exact for it.Which of the following statements about wurtzite and spinel structures are correct?
Show answer
Answer: A — In wurtzite ZnS the S²⁻ ions are hexagonally close-packed and Zn²⁺ occupies half of the tetrahedral voids; D — In magnetite, an inverse spinel, the Fe³⁺ ions are split equally between tetrahedral and octahedral sites
Wurtzite is the HCP form of ZnS with Zn in half the tetrahedral voids. In magnetite, Fe³⁺[Fe²⁺Fe³⁺]O₄, one Fe³⁺ per formula unit is tetrahedral and one is octahedral. In a normal spinel it is A²⁺ that is tetrahedral and B³⁺ that is octahedral, the reverse of the statement, and zinc blende is 4 : 4, not 6 : 6.Which of the following statements about polymer structure are correct?
Show answer
Answer: A — Vulcanised natural rubber cannot be dissolved or remelted into a flowing liquid, because its chains are linked into a covalent network; C — Isotactic and syndiotactic chains are regular enough to crystallise, whereas atactic chains of a bulky side-group polymer usually cannot
Crosslinks make rubber a network, which swells but does not dissolve or flow. Regular chains crystallise and atactic bulky-side-group chains do not. Secondary bonds are weaker, not stronger, than covalent ones. The PTFE unit (100.02 g/mol) is heavier than the PVC unit (62.50 g/mol), so the statement about molar masses is false.Sodium chloride has the rock-salt structure with lattice parameter a = 0.5640 nm. Take M(Na) = 22.99 g/mol, M(Cl) = 35.45 g/mol and N_A = 6.022 × 10²³ mol⁻¹. Calculate its theoretical density in g/cm³, to two decimal places.
Numerical answer — type the value.
Show answer
Answer: 2.16
The cell holds 4 formula units. V_c = (0.5640 × 10⁻⁷ cm)³ = 1.7940 × 10⁻²² cm³. ρ = 4 × 58.44/(1.7940 × 10⁻²² × 6.022 × 10²³) = 233.76/108.04 = 2.16 g/cm³. Counting 8 formula units would double it to 4.32.For the cubic perovskite BaTiO₃ use the ionic radii r(Ba²⁺, coordination 12) = 0.161 nm, r(Ti⁴⁺, coordination 6) = 0.0605 nm and r(O²⁻) = 0.140 nm. Compute the Goldschmidt tolerance factor t = (r_A + r_O)/[√2 (r_B + r_O)] to two decimal places.
Numerical answer — type the value.
Show answer
Answer: 1.06
Numerator: 0.161 + 0.140 = 0.301 nm. Denominator: √2 × (0.0605 + 0.140) = 1.4142 × 0.2005 = 0.28355 nm. t = 0.301/0.28355 = 1.0615, that is 1.06. A value above 1 means the A–O distance is too large for the B–O distance, which is why the small Ti⁴⁺ can shift off centre.Polyvinyl chloride has the repeat unit –CH₂–CHCl–. Take C = 12.01, H = 1.008 and Cl = 35.45 g/mol. A sample has a number-average molar mass M̄_n = 75 000 g/mol. Using DP = M̄_n/m, with m the molar mass of one repeat unit, find the number-average degree of polymerisation, rounded to the nearest integer.
Numerical answer — type the value.
Show answer
Answer: 1200
The repeat unit is C₂H₃Cl: m = 2 × 12.01 + 3 × 1.008 + 35.45 = 24.02 + 3.024 + 35.45 = 62.494 g/mol. DP = 75 000/62.494 = 1200.1, so 1200. Using the mass of the vinyl chloride molecule is the same here; using the two-carbon backbone count 2n instead would double the answer.A polyethylene sample has density ρ_s = 0.945 g/cm³. Take the density of the fully crystalline polymer ρ_c = 1.000 g/cm³ and of the fully amorphous polymer ρ_a = 0.870 g/cm³. Use the mass-fraction relation X_c = ρ_c(ρ_s − ρ_a)/[ρ_s(ρ_c − ρ_a)]. Find the percentage crystallinity, rounded to the nearest integer.
Numerical answer — type the value.
Show answer
Answer: 61
X_c = 1.000 × (0.945 − 0.870)/[0.945 × (1.000 − 0.870)] = 0.0750/0.12285 = 0.6105, that is 61 %. Using the simple linear (volume-fraction) interpolation (0.945 − 0.870)/0.130 = 57.7 % ignores that the crystalline mass fraction and volume fraction differ.100 g of natural rubber (repeat unit C₅H₈, 68.12 g/mol) is vulcanised with 5.0 g of sulfur (32.06 g/mol). Assume all the sulfur forms crosslink bridges, each bridge consisting of exactly four S atoms and joining exactly two repeat units, with no repeat unit in more than one bridge. What percentage of the repeat units is crosslinked, to one decimal place?
Numerical answer — type the value.
Show answer
Answer: 5.3
Repeat units = 100/68.12 = 1.468 mol. S = 5.0/32.06 = 0.1560 mol, so bridges = 0.1560/4 = 0.0390 mol. Crosslinked units = 2 × 0.0390 = 0.0780 mol. Fraction = 0.0780/1.468 = 0.0531, that is 5.3 %. Forgetting that each bridge joins two units would give 2.7 %.